Product Name:Epoxy Vinyl Ester Resin HS-4430
1. Brief Introduction:HS-4430 is a premium bisphenol A epoxy vinyl ester resin, meticulously crafted for a variety of FRP applications, including anti-corrosive linings, FRP tanks, electrical insulating materials, and FRP molds. This versatile resin is ideal for hand lay-up, pultrusion, and filament winding processes. Renowned for its excellent mechanical strength, toughness, and superb heat and corrosion resistance, HS-4430 stands as one of the most superior resins ever designed for the marine industry.
premium resins ever designed for the marine industry.
2. Technical Data Sheet for Liquid Resin:
Item |
Standard Requirements |
Test Method |
Appearance |
Yellow Transparent Liquid |
GB/T 8237.6.1.1 |
Viscosity(25ºC,cP) |
400-500 |
GB/T 7193.4.1 |
Geltime(25ºC,min) |
10.0-30.0 |
GB/T 7193.4.6 |
Solids Content(%) |
60.0-64.0 |
GB/T 7193.4.3 |
Acid Value(mgKOH/g) |
5.0-13.0 |
GB/T 2895 |
Curing system in GT test: Accelerator 0.6Co/Naph: 2%; Hardener AKZO LPT: 2%;
3. Physical properties of casting (for reference only):
Item |
Unit |
Test Value |
Test Method |
Tensile Strength |
MPa |
90 |
GB/T2568 |
Tensile Modulus |
MPa |
3000 |
GB/T2568 |
Breaking Elongation |
% |
6.3 |
GB/T2568 |
Flexural Strength |
MPa |
140 |
GB/T2570 |
Flexural Modulus |
MPa |
3400 |
GB/T2570 |
Impact Strength |
KJ/m2 |
19.5 |
GB/T2571 |
HDT |
ºC |
105 |
GB/T1634 |
Hardness(Barcol934-1) |
-- |
42 |
GB/T3854 |
Note:
1) The casting is made according to GB/T8237-2005; Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing: RT×24hrs +80ºC×24hrs;
4 . Instruction and attention:1) To minimize bubbles and achieve a broad gel time scale, use a low-activity curing agent like Butanox LPT from AKZO. When used as an overcoat layer (such as the outermost layer of pipelines and tanks), paraffin must be added to ensure the desired curing degree.
When used as an overcoat layer (such as the outermost layer of pipelines and tanks), paraffin must be added to ensure the expected curing degree.
2) The recommended addition is 300ppm (melting point 52~57ºC). Additionally, to maximize the benefits of paraffin, ensure the resin has a short gel time (approximately 30 minutes).
3)To minimize bubbles and achieve a broad gel time scale, use a low-activity curing agent like Butanox LPT from AKZO. When used as an overcoat layer (such as the outermost layer of pipelines and tanks), paraffin must be added to ensure the desired curing degree. The recommended addition is300ppm (melting point 52~57ºC). Additionally, to maximize the benefits of paraffin, ensure the resin has a short gel time (approximately 30 minutes).300ppm (melting point 52~57ºC). Additionally, to maximize the benefits of paraffin, ensure the resin has a short gel time (approximately 30 minutes).
5. Storage:
1) Avoid exposure to heat sources such as direct sunlight or steam pipes. Store in a dry place at temperatures below 25ºC.
2) Keep sealed to prevent moisture absorption and monomer loss. Prolonged storage outside recommended conditions can affect liquid resin properties such as viscosity and gel time.
3) Transportation should comply with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations'. Due to its styrene monomer content, it is classified as hazardous and flammable.