Carbon Fiber Reinforced SMC Resin for Automotive Headlight Support Structures

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Light Yellow Transparent Liquid
• Model NO.: HS-1520
• Viscosity 25°c: 600-800mPa.S
• Solid Content: 12.5-15.5mgKOH/g
• SPI-GT: 6.0-8.0min
• SPI-CT: 7.0-10.0min
• SPI-PET: 240-260ºC
• Water Content: ≤0.08%
• Transport Package: IBC Tank/Drum
• Specification: NPGl type
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name: HS-1520 Unsaturated Polyester Resin

1. Brief Introduction:HS-1520 is a high-quality NPGl type unsaturated polyester resin specifically designed for SMC / BMC applications.It boasts high reactivity, low viscosity, and excellent coloring and thickening properties.The product's surface is impeccably flat, providing a high-gloss finish that significantly enhances the final product's aesthetic appeal.With outstanding water resistance, heat resistance, high mechanical strength, and superior electrical performance,HS-1520 has become a staple in the automotive industry.Utilizing this advanced resin technology results in carbon fiber SMC structural composites that offer exceptional mechanical properties. Benefits include mass reduction, low tooling costs, noise reduction, and resilience against heat and corrosion.HS-1520resin system in structural applications.
2. Technical Data Sheet for Liquid Resin:

Item	Unit	Standard Requirements	Test Method
Appearance	---	Light yellow slightly turbid liquid	GB/T 8237.6.1.1
Viscosity	25ºC,mPa.s	600-800	GB/T 7193.4.1
SPI-GT	min	6.0-8.0	HK-D-DB001
SPI-CT	min	7.0-10.0	HK-D-DB001
SPI-PET	ºC	240-260	HK-D-DB001
Acid Value	mgKOH/g	12.5-15.5	GB/T 2895
Solid Content	%	59.0-63.0	GB/T 7193.4.3
Water Content	%	≤0.08	HK-D-DB007
Color Code	---	≤35	HK-D-DB036

Note:
SPI: 2% BPO paste.

3. Physical Properties of Casting (for reference only):

Item	Unit	Series Test Value	Test Method
Tensile Strength	MPa	50	GB/T 2568
Tensile Modulus	MPa	3000	GB/T 2568
Tensile Elongaton	%	1.5	GB/T 2568
Flexural Strength	MPa	100	GB/T 2570
Flexural Modulus	MPa	3300	GB/T 2570
Impact Toughness	kJ/m^2	8.5	GB/T 2571
HDT	ºC	130	GB/T 1634
Barcol Hardness	--	48	GB/T 3854

Note:
1) Method for making of cured performed as GB/T 8237, Curing system: 0.6% Co-Naph: 1.5%,
AKZO M-50: 1.5%;
2) Post-cure: room temperature × 24h + 60ºC × 3h + 110ºC × 2h.

4. Storage:
Store the product in a cool place, keeping it under25 ºC, away from fires, heat sources,and seal it to prevent the intrusion of moisture, monomers, and volatile substances. Under ambient temperatures up to 25 ºC, the shelf life is 6 months.