Vinyl ester for pultrusion molding used in communication applications fiber optic cables

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4483B
• Viscosity(25ºC): 350-450cP
• SPI-CT(25ºC): 8.0-13.0min
• Transport Package: IBC Tank/Drum
• Specification: Vinyl Ester Resin
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name:Vinyl Ester Resin HS-4483B

1. Brief Introduction:HS-4483B is a high-performance vinyl ester resin meticulously engineered for rapid pultrusion molding. Exhibiting moderate viscosity and high reactivity, HS-4483B significantly enhances pultrusion line speed while improving surface gloss, minimizing shrinkage, and mitigating internal microphase cracking. The resulting pultrusion products boast superior corrosion resistance, exceptional mechanical properties, and excellent electrical characteristics. HS-4483B is particularly ideal for manufacturing fiber optic cable strengthening core, meeting the demanding requirements of the communication industry.
Products manufactured with HS-4483B demonstrate outstanding mechanical and electrical properties, coupled with robust corrosion resistance. HS-4483B is especially suitable for the production of fiber optic cable strengthening cores, ensuring reliability and durability in high-performance communication applications.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	350-450	GB/T 7193.4.1
SPI-GT(25ºC,min)	8.0-13.0	GB/T 7193.4.6

Curing System in GT Test: Hardener AKZO CH-50: 2%;
3. Physical Properties of Casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	77	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	3.5	GB/T2568
Flexural Strength	MPa	120	GB/T2570
Flexural Modulus	MPa	3350	GB/T2570
Impact Strength	KJ/m^2	7	GB/T2571
HDT	ºC	130	GB/T1634
Hardness(Barcol 934-1)	--	41	GB/T3854

Note:
1) The casting is prepared in compliance with GB/T8237-2005 standards; Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post Curing Process: RT
×
24 hrs +60
ºC ×
3 hrs +120
ºC ×
2 hrs;

4. Storage:
1) Avoid exposure to heat sources such as direct sunlight or steam pipes. Store in a dry place at temperatures not exceeding 25ºC.
2) Keep the container sealed to prevent moisture absorption and monomer loss. Prolonged storage outside recommended conditions can affect resin properties like viscosity and gel time.
3) Ensure transportation complies with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations.' Due to the presence of styrene monomer, the product is classified as hazardous and inflammable.

Packaging & Shipping

Application

Certifications

FAQ