Liquid resin for pultrusion molding in communication fiber optic cable applications

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4483B
• Viscosity(25ºC): 350-450cP
• SPI-CT(25ºC): 8.0-13.0min
• Transport Package: IBC Tank/Drum
• Specification: Vinyl Ester Resin
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name:Vinyl Ester Resin HS-4483B

1. Brief Introduction:HS-4483B is a specialized vinyl ester resin designed for rapid pultrusion molding. This resin boasts moderate viscosity and high reactivity, significantly enhancing pultrusion line speed. Its formulation not only improves product surface gloss but also minimizes shrinkage and internal microphase cracks. Pultrusion products crafted with HS-4483B exhibit excellent corrosion resistance, mechanical properties, and electrical properties. HS-4483B is particularly ideal for manufacturing the strengthening core of fiber optic cables.
products produced by HS-4483B have great corrosion resistance, mechanical properties, and electrical properties. HS-4483B is especially suitable for the production of fiber optic cable strengthening core.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	350-450	GB/T 7193.4.1
SPI-GT(25ºC,min)	8.0-13.0	GB/T 7193.4.6

Curing system in GT test: Hardener AKZO CH-50: 2%;
3. Physical properties of casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	77	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	3.5	GB/T2568
Flexural Strength	MPa	120	GB/T2570
Flexural Modulus	MPa	3350	GB/T2570
Impact Strength	KJ/m^2	7	GB/T2571
HDT	ºC	130	GB/T1634
Hardness(Barcol 934-1)	--	41	GB/T3854

Note:
1) The casting is produced according to GB/T8237-2005 standards. Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing:RT
×
24hrs +60
ºC×
3hrs +120
ºC×
2hrs;

4. Storage:
1) Avoid exposure to heat sources like direct sunlight or steam pipes. Store in a dry place at temperatures below 25ºC.
2) Ensure the container is sealed to prevent moisture absorption and monomer loss. Extended storage outside recommended conditions can affect liquid resin properties, such as viscosity and gel time.
3) Transportation must comply with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations.' Due to its styrene monomer content, it is classified as hazardous and inflammable.

Packaging & Shipping

Application

Certifications

FAQ