Resin for fiber optic cable core used in pultrusion molding communication

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4483B
• Viscosity(25ºC): 350-450cP
• SPI-CT(25ºC): 8.0-13.0min
• Transport Package: IBC Tank/Drum
• Specification: Vinyl Ester Resin
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name:Vinyl Ester Resin HS-4483B

1. Brief Introduction:HS-4483B is a specialized vinyl ester resin crafted for rapid pultrusion molding. Featuring moderate viscosity and high reactivity, it significantly boosts pultrusion line speed while enhancing the product’s surface gloss and reducing shrinkage and internal microphase cracks.
Products manufactured with HS-4483B exhibit remarkable corrosion resistance, superior mechanical properties, and excellent electrical properties. It is especially ideal for producing fiber optic cable strengthening cores.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	350-450	GB/T 7193.4.1
SPI-GT(25ºC,min)	8.0-13.0	GB/T 7193.4.6

Curing system in GT test: Hardener AKZO CH-50: 2%;
3. Physical properties of casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	77	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	3.5	GB/T2568
Flexural Strength	MPa	120	GB/T2570
Flexural Modulus	MPa	3350	GB/T2570
Impact Strength	KJ/m^2	7	GB/T2571
HDT	ºC	130	GB/T1634
Hardness(Barcol 934-1)	--	41	GB/T3854

Note:
1) The casting follows GB/T8237-2005 standards; Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing: RT
×
24hrs +60
ºC×
3hrs +120
ºC×
2hrs;

4. Storage:
1) Store away from heat sources such as direct sunlight or steam pipes in a dry place below 25ºC.
2) Keep sealed to avoid moisture absorption and monomer loss. Extended storage outside recommended conditions may affect liquid resin properties like viscosity and gel time.
3) Transportation should comply with State Council's 'Chemistry Dangerous Articles Safety Management Regulations.' Containing styrene monomer, it classifies as hazardous and inflammable.