Carbon Fiber Reinforced SMC Resin for Automotive Headlight Support Applications

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Light Yellow Transparent Liquid
• Model NO.: HS-1520
• Viscosity 25°c: 600-800mPa.S
• Solid Content: 12.5-15.5mgKOH/g
• SPI-GT: 6.0-8.0min
• SPI-CT: 7.0-10.0min
• SPI-PET: 240-260ºC
• Water Content: ≤0.08%
• Transport Package: IBC Tank/Drum
• Specification: NPGl type
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

 

Product Name: HS-1520 Unsaturated Polyester Resin

1. Brief Introduction:HS-1520 is a premium-grade NPGl type unsaturated polyester resin meticulously engineered for SMC / BMC applications.It boasts high reactivity, low viscosity, and excellent coloring and thickening properties.The product's surface is impeccably smooth, delivering a high gloss finish that amplifies the final product's aesthetic appeal.Offering superb water resistance, impressive heat resistance, high mechanical strength, and excellent electrical performance,HS-1520 is extensively utilized within the automotive industry.Components crafted with this advanced resin technology yield carbon fiber SMC structural composites with exceptional mechanical properties. Benefits include significant mass reduction, minimized tooling costs, noise reduction, and enhanced heat and corrosion resistance.HS-1520resin system in structural applications.
2.Technical Data Sheet for Liquid Resin:

Item	Unit	Standard Requirements	Test Method
Appearance	---	Light yellow slightly turbid liquid	GB/T 8237.6.1.1
Viscosity	25ºC,mPa.s	600-800	GB/T 7193.4.1
SPI-GT	min	6.0-8.0	HK-D-DB001
SPI-CT	min	7.0-10.0	HK-D-DB001
SPI-PET	ºC	240-260	HK-D-DB001
Acid Value	mgKOH/g	12.5-15.5	GB/T 2895
Solid Content	%	59.0-63.0	GB/T 7193.4.3
Water Content	%	≤0.08	HK-D-DB007
Color Code	---	≤35	HK-D-DB036

 

Note:
SPI: 2% BPO paste.

3. Physical Properties of Casting (for reference only):

Item	Unit	Series Test Value	Test Method
Tensile Strength	MPa	50	GB/T 2568
Tensile Modulus	MPa	3000	GB/T 2568
Tensile Elongaton	%	1.5	GB/T 2568
Flexural Strength	MPa	100	GB/T 2570
Flexural Modulus	MPa	3300	GB/T 2570
Impact Toughness	kJ/m^2	8.5	GB/T 2571
HDT	ºC	130	GB/T 1634
Barcol Hardness	--	48	GB/T 3854

 

Note:
1) Method for making cured performed as per GB/T 8237, Curing system: 0.6% Co-Naph: 1.5%,
AKZO M-50: 1.5%;
2) Post-cure: room temperature × 24h + 60ºC × 3h + 110ºC × 2h.

4. Storage:
The product should be stored in a cool place under25 ºC, away from flames, heat sources,and sealed to prevent the intrusion of moisture, monomers, and volatile substances. For long-term storage under an ambient temperature of 25 ºC, the shelf life is 6 months.