Vinyl ester for communication applications in fiber optic cable pultrusion

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4483B
• Viscosity(25ºC): 350-450cP
• SPI-CT(25ºC): 8.0-13.0min
• Transport Package: IBC Tank/Drum
• Specification: Vinyl Ester Resin
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name:Vinyl Ester Resin HS-4483B

1. Brief Introduction:HS-4483B is a meticulously engineered vinyl ester resin, purpose-built for high-speed pultrusion molding. Featuring moderate viscosity and high reactivity, it significantly accelerates pultrusion line speeds. This advanced resin not only enhances product surface gloss but also minimizes shrinkage and internal microphase cracking. Pultrusion products crafted using HS-4483B boast exceptional corrosion resistance, mechanical integrity, and electrical properties. HS-4483B is the optimal choice for manufacturing fiber optic cable strengthening cores.
Pultrusion products produced by HS-4483B possess outstanding corrosion resistance, superior mechanical properties, and excellent electrical characteristics. HS-4483B is particularly ideal for the production of fiber optic cable strengthening cores.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	350-450	GB/T 7193.4.1
SPI-GT(25ºC,min)	8.0-13.0	GB/T 7193.4.6

Curing system in GT test: Hardener AKZO CH-50: 2%;
3. Physical properties of casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	77	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	3.5	GB/T2568
Flexural Strength	MPa	120	GB/T2570
Flexural Modulus	MPa	3350	GB/T2570
Impact Strength	KJ/m^2	7	GB/T2571
HDT	ºC	130	GB/T1634
Hardness(Barcol 934-1)	--	41	GB/T3854

Note:
1) The casting is prepared following GB/T8237-2005 standards; Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing: RT
×
24hrs + 60
ºC ×
3hrs + 120
ºC ×
2hrs;

4. Storage:
1) Store in a dry place away from heat sources like direct sunlight or steam pipes, at temperatures below 25ºC.
2) Ensure containers are sealed to prevent moisture absorption and monomer loss. Extended storage beyond recommended conditions may affect the liquid resin's properties such as viscosity and gel time.
3) Transportation should comply with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations'. Due to the presence of styrene monomer, this product is classified as hazardous and flammable.

Packaging & Shipping

Application

Certifications

FAQ