Self Leveling Floor Paint Clear Epoxy Resin Texture Epoxy Curing Agent Liquid Coating for Bathroom Floor Customized

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4430
• Viscosity(25ºC): 400-500cP
• Geltime(25ºC): 10-30min
• Solid Content: 60.0-64.0%
• Acid Value: 5.0-13.0mgKOH/g
• Transport Package: IBC Tank/Drum
• Specification: Bisphenol A Epoxy Vinyl Ester
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

 

Product Name: CCS Certified Marine Epoxy Resin for Chemical Resistant and Heat Resistant FRPEpoxyVinyl Ester Resin HS-4430

1. Brief Introduction:HS-4430 is a premium-grade bisphenol A epoxy vinyl ester resin, meticulously engineered for the production of various FRP applications. These encompass anti-corrosive linings, FRP tanks, electrical insulating materials, and FRP molds. Designed for versatility, HS-4430 excels in hand lay-up, pultrusion, and filament winding processes. This resin boasts excellent mechanical strength, remarkable toughness, and superior heat and corrosion resistance, making it an outstanding choice for the marine industry.
It is one of the premium resins ever designed for the marine industry.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	400-500	GB/T 7193.4.1
Geltime(25ºC,min)	10.0-30.0	GB/T 7193.4.6
Solids Content(%)	60.0-64.0	GB/T 7193.4.3
Acid Value(mgKOH/g)	5.0-13.0	GB/T 2895

 

Curing system in GT test: Accelerator 0.6Co/Naph: 2%; Hardener AKZO LPT: 2%;
3. Physical properties of casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	90	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	6.3	GB/T2568
Flexural Strength	MPa	140	GB/T2570
Flexural Modulus	MPa	3400	GB/T2570
Impact Strength	KJ/m^2	19.5	GB/T2571
HDT	ºC	105	GB/T1634
Hardness(Barcol934-1)	--	42	GB/T3854

 

Note:
1) The casting is manufactured according to GB/T8237-2005 standards. Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing: RT×24hrs + 80ºC×24hrs;

4 . Instruction and attention:1) To minimize bubble formation and achieve an extended gel time, use a low-activity curing agent such as AKZO's Butanox LPT.
When applied as an overcoat layer, such as the outermost layer of a pipeline or tank, paraffin must be added to ensure the resin cures as expected.
2) The recommended paraffin addition is 300ppm (melting point 52~57ºC). To maximize the effectiveness of paraffin, aim for a short gel time (approximately 30 minutes).
3)To minimize bubble formation and achieve an extended gel time, use a low-activity curing agent such as AKZO's Butanox LPT. When applied as an overcoat layer, such as the outermost layer of a pipeline or tank, paraffin must be added to ensure the resin cures as expected. The recommended paraffin addition is300ppm (melting point 52~57ºC). To maximize the effectiveness of paraffin, aim for a short gel time (approximately 30 minutes).300ppm (melting point 52~57ºC). To maximize the effectiveness of paraffin, aim for a short gel time (approximately 30 minutes).
5. Storage:
1) Avoid exposure to heat sources such as direct sunlight or steam pipes. Store in a dry place at temperatures below 25ºC.
2) Keep sealed to prevent moisture absorption and monomer loss. Prolonged storage outside recommended conditions can affect the resin's viscosity and gel time.
3) Transportation should comply with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations.' As the resin contains styrene monomer, it is hazardous and flammable.

Packaging & Shipping

Application

 

 

Certifications

 

 

 

FAQ