Allnex TMPTA Trimethylolpropane Triacrylate UV cured resin coating diluent

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Light Yellow Transparent Liquid
• Model NO.: UV-2301
• Viscosity (25ºC): 400-500mPa·s
• Solid Content: 52-58%
• Transport Package: IBC Tank/Drum
• Specification: ISO/NPG
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

 

Product Name:UV-2301 UV-curable Unsaturated Polyester Resin

1. Brief Introduction:
UV2301 is a highly reactive and medium-viscosity isophthalate neopentylene glycol type unsaturated polyester resin. With magnesium oxide, it is stable and thickened, can be cured by ultraviolet lamp, has excellent glass fiber wettability, fast curing speed and excellent mechanical properties. It is suitable for ultraviolet curing trenchless repair (CIPP) of sewer pipelines, oil and gas pipelines.
2.Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Light yellow transparent liquid	GB/T 8237.6.1.1
Viscosity(25ºC, mPa.s)	400-500	GB/T 7193.4.1
Solid Content (%)	52.0-58.0	GB/T 7193.4.3

 

Curing system in SPI test:Hardener AKZO CH-50: 2%;
3. Physical properties of casting(for reference only):

Item	Unit	Test Value	Test Method
Tensile strength	MPa	80	GB/T 2568
Tensile modulus	MPa	3000	GB/T 2568
Breaking elongation	%	4.2	GB/T 2568
Flexural strength	MPa	142	GB/T 2570
Flexural modulus	MPa	3400	GB/T 2570
Hardness (Barcol 934-1)	--	40	GB/T 3854
HDT	ºC	105	GB/T 1634

 

Note:The casting is made according to GB/T8237; Curing conditions: UV LED LS128 light intensity 14mW/cm2
, 5min.
4 . Suggestions for use:1) UV2301 resin can be thickened with magnesium oxide paste. There is a direct relationshipwith the model and amount of magnesium oxide paste on the thickening viscosity andthickening rate.So, small batch trials are recommended before use.
2) UV2301 resin can be curedby *** lamp and UV-LED lamp, if you need to use other light sources for curing, please do small-batch trialsin advance.
5. Storage:
1) The product should be packaged in black IBC tank or iron drum, as the resin contains ultraviolet light initiator, the packaging drum must be placed in a dark place and kept 100% opaque.
2) Transportation should fit the State Council "Chemistry Dangerous Articles Safety Management Regulations".
3) Avoid exposure to heat sources such as direct sunlight or steam pipes. Keep sealed to prevent moisture pick-up and monomer loss. Stored in a dry place at temperatures below 25ºC and the shelf life is 6 months.
The storage time decreases with increasing temperature.