Xinshen/Huake HS-4483B Vinyl Ester Resin for Communication Cables

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Yellow Transparent Liquid
• Model NO.: HS-4483B
• Viscosity(25ºC): 350-450cP
• SPI-CT(25ºC): 8.0-13.0min
• Transport Package: IBC Tank/Drum
• Specification: Vinyl Ester Resin
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

Product Name:Vinyl Ester Resin HS-4483B

1. Brief Introduction:HS-4483B is a premium vinyl ester resin meticulously crafted for rapid pultrusion molding. With its moderate viscosity and high reactivity, this resin significantly accelerates the pultrusion line speed. It enhances product surface gloss, minimizes shrinkage, and reduces internal microphase cracks. Pultrusion
products made with HS-4483B boast exceptional corrosion resistance, superior mechanical properties, and outstanding electrical performance. HS-4483B is the ideal choice for producing the fiber optic cable strengthening core.
2. Technical Data Sheet for Liquid Resin:

Item	Standard Requirements	Test Method
Appearance	Yellow Transparent Liquid	GB/T 8237.6.1.1
Viscosity(25ºC,cP)	350-450	GB/T 7193.4.1
SPI-GT(25ºC,min)	8.0-13.0	GB/T 7193.4.6

Curing system in GT test: Hardener AKZO CH-50: 2%;
3. Physical properties of casting (for reference only):

Item	Unit	Test Value	Test Method
Tensile Strength	MPa	77	GB/T2568
Tensile Modulus	MPa	3000	GB/T2568
Breaking Elongation	%	3.5	GB/T2568
Flexural Strength	MPa	120	GB/T2570
Flexural Modulus	MPa	3350	GB/T2570
Impact Strength	KJ/m^2	7	GB/T2571
HDT	ºC	130	GB/T1634
Hardness(Barcol 934-1)	--	41	GB/T3854

Note:
1) The casting is made according to GB/T8237-2005; Curing System: Accelerator KC: 1.0%;
Hardener AKZO LPT: 1.0%;
2) Post curing:RT
×
24hrs +60
ºC×
3hrs +120
ºC×
2hrs;

4. Storage:
1) Avoid exposure to heat sources such as direct sunlight or steam pipes. Store in a dry place at temperatures below 25ºC.
2) Keep sealed to prevent moisture absorption and monomer loss. Prolonged storage outside recommended conditions can affect properties like viscosity and gel time.
3) Transportation should comply with the State Council's 'Chemistry Dangerous Articles Safety Management Regulations.' Containing styrene monomer, this product is hazardous and inflammable.

Packaging & Shipping

Application

Certifications

FAQ