89 UPR Marine fiberglass unsaturated polyester resin for FRP products

• Customization: Available
• Molecular Principal Chain: Carbon Chain Polymer
• Color: Light Yellow Slightly Turbid Liquid
• Model NO.: HS-1520
• Viscosity 25°c: 600-800MPa.S
• Acid Value: 12.5-15.5mgkoh/G
• Solid Content: 59.0-63.0%
• Spi-Gt: 6.0-8.0min
• Spi-CT: 7.0-10.0min
• Water Content: ≤0.08%
• Color Code: ≤35
• Transport Package: IBC Tank
• Specification: NPGl type
• Trademark: Xinshen/Huake
• Origin: Jiangsu, China
• HS Code: 3907910000
• Production Capacity: 100000 Ton/Year

Product Description

Product Description

 

Product Name: HS-1520 Unsaturated Polyester Resin

1. Brief Introduction:HS-1520is a top-tier NPGl type unsaturated polyester resin specifically designed for SMC/BMC applications. This resin boasts exceptional reactivity,
low viscosity, outstanding coloring, and superior thickening properties. The end product exhibits a remarkably smooth surface withhigh gloss, superior water resistance, excellent heat resistance, impressive mechanical strength, and exceptionalelectrical performance. This makes it ideal for use in electrical components, industrial parts, sanitary fixtures, automotiveparts, and various other fields.

2. Technical Data Sheet for Liquid Resin:

Item	Unit	Standard Requirements	Test Method
Appearance	---	Light yellow slightly turbid liquid	GB/T 8237.6.1.1
Viscosity	25ºC,mPa.s	600-800	GB/T 7193.4.1
SPI-GT	min	6.0-8.0	HK-D-DB001
SPI-CT	min	7.0-10.0	HK-D-DB001
SPI-PET	ºC	240-260	HK-D-DB001
Acidvalue	mgKOH/g	12.5-15.5	GB/T 2895
Solidcontent	%	59.0-63.0	GB/T7193.4.3
Watercontent	%	≤0.08	HK-D-DB007
Colorcode	---	≤35	HK-D-DB036

 

Note:
SPI: 2% BPO paste.

3. Physical Properties of Casting (for reference only):

Item	Unit	Series Test Value	Test Method
Tensile strength	MPa	50	GB/T 2568
Tensile modulus	MPa	3000	GB/T 2568
Tensile elongaton	%	1.5	GB/T 2568
Flexural strength	MPa	100	GB/T 2570
Flexural modulus	MPa	3300	GB/T 2570
Impact toughness	kJ/m2	8.5	GB/T 2571
HDT	ºC	130	GB/T 1634
Barcol hardness	--	48	GB/T 3854

 

Note:
1) Method for making of cured performed as per GB/T 8237, Curing system: 0.6% Co-Naph, 1.5%,
AKZO M-50: 1.5%;
2) Post-cure: room temperature × 24h + 60ºC × 3h + 110ºC × 2h.

4. Storage:
This product should be stored in a cool, dry place under25ºC, away from open flames, heat sources,and should be sealed to prevent moisture, monomer, and volatile substance intrusion. For extended storage at ambient temperatures up to 25ºC, the shelf life is 6 months.